New method claims to improve strength and modulus in carbon fiber

The group used a gel-spinning technique to process polyacrylonitrile copolymer into carbon fibers.

Author:
Posted on: 7/30/2015
Source: CompositesWorld

Click Image to Enlarge

Photograph shows a high strength and high modulus carbon fiber processed at Georgia Tech. (Credit: Gary Meek, Georgia Tech).

A research team at the Georgia Institute of Technology believes it has developed a novel technique that could set a new milestone for the strength and modulus of carbon fibers. The group developed an alternative approach that is based on an innovative technique for spinning polyacrylonitrile (PAN), an organic polymer resin used to make carbon fibers.

The work is part of a four-year, $9.8 million project sponsored by the Defense Advanced Research Projects Agency (DARPA) to improve the strength of carbon fiber materials. The research was reported recently in the journal Carbon.

"By using a gel-spinning technique to process polyacrylonitrile copolymer into carbon fibers, we have developed next-generation carbon fibers that exhibit a combination of strength and modulus not seen previously with the conventional solution-spun method," said Satish Kumar, a professor in the Georgia Tech School of Materials Science and Engineering who leads the project. “In addition, our work shows that the gel-spinning approach provides a pathway for even greater improvements.”

In gel-spinning, the solution is first converted to a gel. This technique binds polymer chains together and produces robust inter-chain forces that increase tensile strength. Gel-spinning also increases directional orientation of fibers, which also augments strength. 

The gel-spun carbon fiber produced by Kumar’s team was tested at 5.5 to 5.8 gigapascals (GPa) – a measure of ultimate tensile strength – and had a tensile modulus in the 354-375 GPa range. The material was produced on a continuous carbonization line at Georgia Tech that was constructed for this DARPA project.

“This is the highest combination of strength and modulus for any continuous fiber reported to-date,” Kumar said. “And at short gauge length, fiber tensile strength was measured as high as 12.1 GPa, which is the highest tensile-strength value ever reported for a PAN-based carbon fiber.”

Kumar said that the internal structure of these gel-spun carbon fiber measured at the nanoscale showed fewer imperfections than state-of-the-art commercial carbon fibers, such as IM7. Specifically, the gel-spun fibers display a lower degree of polymer-chain entanglements than those produced by solution spinning. This smaller number of entanglements results from the fact that gel-spinning uses lower concentrations of polymer than solution-spinning methods.

Kumar and his team convert the gel-spun polymer mix into carbon fibers via a selective treatment process called pyrolysis, in which the spun polymer is gradually subjected to both heat and stretching. This technique eliminates large quantities of hydrogen, oxygen, and nitrogen from the polymer, leaving mostly strength-increasing carbon.

“It’s important to remember that the current performance of solution-spun PAN-based carbon fibers has been achieved after many years of material and process optimization – yet very limited material and process optimization studies have been carried out to date on the gel-spun PAN fiber,” Kumar said. “In the future, we believe that materials and process optimization, enhanced fiber circularity, and increased solution homogeneity will further increase the strength and modulus of the gel-spinning method.”